Petroleum,petrochemical and natural gas industries —Test methods for quality control  of  microstructure  of  ferritic/austenitic(duplex)stainless  steels

石油、石化和天然氣工業鐵素體/奧氏體(雙相)不鏽鋼微觀結構質量控製的試驗方法

1 Scope

1範圍

This document specifies quality control testing methods and test conditions for the characterization of  microstructure in relation to relevant properties in

ferritic/austenitic(duplex)stainless  steel  components supplied in the solution annealed condition and fabrication welds in the as welded condition.

本文件規定了在固溶退火條件下供應的鐵素體/奧氏體(雙相)不鏽鋼部件和在焊接狀態下的製造焊縫的微觀結構表征 的質量控製測試方法和測試條件。

This document supplements the relevant product and fabrication standards with respect to destructive

testing methods including sampling of test specimens,test conditions and test acceptance criteria to show freedom from deleterious intermetallic phases and precipitates in duplex stainless steels.In addition,this    document specifies the documentation of testing and test results by the testing laboratory.

本文件補充了有關破壞性測試方法的相關蜜桃视频APP入口和製造標準，包括試樣取樣、測試條件和測試驗收標準，以表明雙相不鏽鋼中沒有有害的金屬間相和沉澱物。此外，本文件規定了測試實驗室的測試和測試結果文件。

NOTE 1:This document is based upon experience with duplex stainless steels in offshore oil and gas industry applications including topside and subsea hydrocarbon service,sea water service,as well as structural use.

注1:本文件基於雙相不鏽鋼在海上石油和天然氣行業應用的經驗，包括上部和海底碳氫化合物服務、海水服務以及結構用途。

NOTE 2:The austenite spacing is relevant to the susceptibilityof duplex stainless steels to hydrogen-induced

stress cracking(HISC)in subsea applications where cathodic protection is applied.This falls outside the scope of this document.Reference is made to DNV/GL RP-F112 [4].

注2:在采用陰極保護的海底應用中，奧氏體間距與雙相不鏽鋼對氫致應力開裂(HISC)的敏感性有關。這不屬於本文件的範圍。參考DNV/GLRP-F112[4]。

ISO   148-1,Metallic  materials  —Charpy  pendulum  impact  test—Part  1:Test  method

ISO   148-1,金屬材料—夏比擺錘衝擊試驗—第1部分：試驗方法